Mechanical Properties of Steel 1018HR 1018CD 1045HR 304SS Young's Modulus [GPa] 192 241 240 281 Rockwell hardness (previous to tension test) [HRB] 72.68 94.24 98.22 83.48 Yield Strength [MPa] 329 612 495 256 Tensile Strength [MPa] 492 671 808 588 Elongation in 50 mm at the onset of necking [%] 14.3 3.35 10.54 54.93 Elongation in 50 mm after fracture [%] 32.93 11.67 21.66 74.55 Reduction in area after fracture [%] 65.21 54.56 36.31 81.38 Strain hardening exponent n 0.25 0.05 0.22 0.37 Strength coefficient K [MPa] 933 815 1520 1107 Yield Point Phenomenon (Y/N) Y N Y N 1018HR 1018CD 1045HR 304SS Young's Modulus [GPa] 255 249 156 259 Rockwell hardness (previous to tension test) [HRB] 71.34 91.22 73.2 82.22 Yield Strength [MPa] 323 594 390 262 Tensile Strength [MPa] 477 639 490 593 Elongation in 50 mm at the onset of necking [%] 29.21 3.86 19.00 57.38 Elongation in 50 mm after fracture [%] 28.39 16.30 34.32 81.10 Reduction in area after fracture [%] 67.58 27.97 68.30 81.77 Strain hardening exponent n
Background image of page 1
This is the end of the preview. Sign up to access the rest of the document.

This note was uploaded on 03/01/2010 for the course ME Materials taught by Professor Kuilik during the Spring '08 term at University of Texas at Austin.

Ask a homework question - tutors are online